W6Mo5Cr4V2(M2) hot rolled steel round bars

Classification :

M2 is a molybdenum high-speed steel, which has the advantages of small carbide non-uniformity and high toughness. It is easy to overheat, so the quenching temperature should be strictly controlled, and the protection requirements for heat treatment should be strict

Bella@zglcmetal.com

Execution Standard	ZEICIN Grade	GB	AISI	JIS	DIN
GB/T9943-2008	M2	W6Mo5Cr4V2	M2	SKH51	1.3343

Chemical Composition of M2 Tool Steel Material

ASTM A681	C	Si	Mn	P	S	Cr	Mo	V	W
M2/ T11302	0.78～0.88	0.20～0.45	0.15～0.40	0.030 Max	0.030 Max	3.75～4.50	4.50～5.50	1.75～2.20	5.50～6.75
DIN 17350	C	Si	Mn	P	S	Cr	Mo	V	W
1.3343/ S6-5-2	0.86～0.94	≤0.45	≤0.40	0.030 Max	0.030 Max	3.80～4.50	4.70～5.20	1.70～2.00	6.00～6.70
GB/T 9943	C	Si	Mn	P	S	Cr	Mo	V	W
W6Mo5Cr4V2	0.80～0.90	0.20～0.45	0.15～0.40	0.030 Max	0.030 Max	3.80～4.40	4.50～5.50	1.75～2.20	5.50～6.75
JIS G4403	C	Si	Mn	P	S	Cr	Mo	V	W
SKH51/SKH9	0.80～0.88	≤0.45	≤0.40	0.030 Max	0.030 Max	3.80～4.50	4.70～5.20	5.90～6.70	1.70～2.10

SAE M2 Tool Steel Material Mechanical Properties

Hardness, Rockwell C (tempered at 621°C, quenched at 1204°C): 62 HRC.

Hardness, Rockwell C (quenched at 1204°C) ): 65 HRC

Forged of M2 HSS Steel metal material

At first, Pre-Heating to 650-750℃，Then heat to forged temperature. Soak at 1204°C, ensure heat thorough. Then start forged, the forged temperature no low than 950℃. After forging, cool slowly.

Heat Treatment of SAE M2 Steel

M2 HSS Steel Annealing

At first, Slowly heat to 871℃，then slowly Cool to 538℃(1000℉) in heat treatment furnace. Then cool in air. After annealing hardness HBS: 255 Max.

M2 tool Steel Hardening

M2 steel having very high hardenability and should be hardened by cooling in still air. The use of a salt bath or controlled atmosphere furnace is desirable to minimize decarburization, and if not available, pack hardening in spent pitch coke is suggested.

Quenching of HSS M2 Steel material

Quenching temperature / ℃ | salt bath furnace: 1204

Quenching temperature / ℃ | controlled atmosphere furnace: 1216

The heat preservation time/min: 5 ~ 15

Quenching medium: Oil cooling

Hardness: 65 HRc Min

Tempering Of HSS M2 Tool Steel

Tempering temperature / ℃ : 540-564

After tempering hardness HRC or higher: 65 Min

warehouse storage

The annual output of the factory is 400,000 tons, and the current inventory is more than 100,000 tons, which can greatly save the purchasing time of customers and ensure the production cycle and product quality of customers. We are a quality partner for domestic and foreign customers. At present, there are 14 steel production lines for processing, bending, coating, heat treatment, cutting, drilling, chamfering, conditioning, surface treatment and 13 sets of processing equipment.

Packing and shipping

Our main products are: carbon steel plate, carbon steel pipe, carbon steel coil, stainless steel plate, stainless steel coil, stainless steel profile, galvanized plate, galvanized coil, color coated steel coil, ppgi/ppgl and a wide range of high quality steel products.

Customer visit

Li Cheng (Shandong) Metal Materials Co., LTD. has the right to import and export, and its products are exported to more than 20 countries in Asia, Africa, Europe, North America and other regions. Complete processing equipment, perfect quality assurance system, well received by customers.We are willing to first-class technology, first-class equipment, first-class service wholeheartedly and friends from all walks of life sincere cooperation!

Cooperation Case

Applicable to construction, petroleum, chemical, electric power, metallurgy, urban gas, heat pipe network, Bridges, railways, vehicles, ships and other industrial fields and construction, infrastructure and other engineering fields. Complete testing equipment, strong technical force, can implement GB, ASTM, JIS, DIN and other standards.

HONOR

Factory

FACTORY

Steel Round Bars